  • Magnetic-properties-of-CoxPt100-x-nanoparticles_2016_Journal-of-Science-Advanced-Materials-and-Devices.pdf.jpg
  • Article


  • Authors: Truong, Thanh Trung; Do, Thi Nhung; Nguyen, Thi Thanh Van; Nguyen, Hoang Nam; Nguyen, Hoang Luong (2016)

  • CoxPt100- x nanoparticles (x=50, 59, and 73) were prepared by the chemical reduction of Cobalt (II) chloride and Chloroplatinic acid, then ultrasonicated for 2 h. After annealing at various temperatures from 450 C to 700 C for 1 h, structure change was observed and samples show hard magnetic prop-erties which depend strongly on chemical composition and annealing temperature. The highest coer-civity value of 1.15 kOe was obtained at room temperature for sample with x =50 annealed at 500 C. Chemical reduction combined with ultrasound is a useful method to prepare CoPt nanoparticles

Browsing by Author Do, Thi Nhung

Jump to: 0-9 A B C D E F G H I J K L M N O P Q R S T U V W X Y Z
or enter first few letters:  
Showing results 1 to 1 of 1
  • Magnetic-properties-of-CoxPt100-x-nanoparticles_2016_Journal-of-Science-Advanced-Materials-and-Devices.pdf.jpg
  • Article


  • Authors: Truong, Thanh Trung; Do, Thi Nhung; Nguyen, Thi Thanh Van; Nguyen, Hoang Nam; Nguyen, Hoang Luong (2016)

  • CoxPt100- x nanoparticles (x=50, 59, and 73) were prepared by the chemical reduction of Cobalt (II) chloride and Chloroplatinic acid, then ultrasonicated for 2 h. After annealing at various temperatures from 450 C to 700 C for 1 h, structure change was observed and samples show hard magnetic prop-erties which depend strongly on chemical composition and annealing temperature. The highest coer-civity value of 1.15 kOe was obtained at room temperature for sample with x =50 annealed at 500 C. Chemical reduction combined with ultrasound is a useful method to prepare CoPt nanoparticles