Title: Structure and Photoluminescence Characterization of LaPO4:Sm3+ Nanowires Prepared by Hydrothermal Method
Authors: Pham, Thi Thanh Hien
Duong, Thi Mai Huong
Nguyen, Ngoc Long
Le, Van Vu
Hoang, Manh Ha
Keywords: Hydrothermal method;samarium doped lanthanum orthophosphate;nanowires
Issue Date: 2015
Publisher: H. : ĐHQGHN
Series/Report no.: Vol.31;No. 4 (2015)
Abstract: LaPO4 nanowires doped with 1, 2,…8 mol% Sm3+ were prepared by a hydrothermal method. The samples were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), photoluminescence (PL), photoluminescence excitation (PLE), and absorption (ABS) spectroscopy. It was discovered that the PL and PLE of Sm3+ ions resulted from the radiative intra-configurational f-f transitions. The photoluminescence spectra shows 4 peaks at 560 nm, 596 nm, 642 nm and 701 nm which were assigned to different transitions from the 4G (4)5/2 excited state to the 6HJ with J = 5/2; 7/2; 9/2; 11/2 ground states of Sm3+ ion. The intensity of PL related to Sm3+ ion reached to a maximum when the Sm doping content was 2 mol%. Diffuse reflective spectra measured at room temperature of the Sm3+ doped LaPO4 exhibited absorption peaks at 343, 362, 374, 401, 415, 439, 460 and 477 nm which were observed in PLE spectra as well.
Description: p. 13-22
URI: http://repository.vnu.edu.vn/handle/VNU_123/55796
ISSN: 2588-1124
Appears in Collections:Mathematics and Physics

Files in This Item:
Thumbnail

  • File : 40.pdf
  • Description : 
  • Size : 448.9 kB
  • Format : Adobe PDF


  • Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.